High purity Fused Silica Crucibles developed by us are internationally unique in that they are produced using high purity Fused Silica and our exclusive, special forming processes. They are applicable to very high temperature (1650℃) while they have very low thermal expansion coefficient. They are ideal for the production of multi(poly)-crystal ingots · wafers for solar cells. Fused Silica Crucibles are used in cutting edge fields with wide variety of applications.
폐사에서 개발한 고순도의 용융석영도가니(Fused Silica Crucible)는 고순도의 Fused Silica 원료를 (주)솔라세라 만의 독보적인 특수성형법으로 제조된 세계유일의 제품으로, 사용 가능 온도가 아주 높고(1650℃), 열팽창계수가 매우 낮은것이 특징으로, 태양전지용 다결정 잉곳(ingot) · 웨이퍼(wafer) 제조에 사용되어지며, 초-고품질을 위한 최첨단 분야에서 다각도로 이용되고 있습니다.
The Most Advanced Cutting Edge Technology of Fused Silica Crucible,
The World's Only Unique Fused Silica Crucible Manufacturer, SOLAR CERA Co.,Ltd.
|
|
| |
|
|
| |
|
|
| |
|
|
| |
[ Characteristics (특징) ]
1. Thermal expansion coefficient (lowest among high temperature materials) is extremely low
2. Very high non-spalling performance
3. Very high thermal resistance against molten steel, impact resistance, wear resistance and anti-erosion performance
4. Very low air permeability
5. Very low thermal conductivity
6. Excellent chemical stability
1. 열팽창 계수가 극히 적다. (고온 재료 중 가장 적다)
2. 내스포링성이 극히 우수하다.
3. 용강에 대한 내열 충격성, 마모성, 내침식성이 아주 우수하다.
4. 통기성이 아주 적다.
5. 열전도도가 아주 적다.
6. 화학적 안정성이 아주 우수하다.
|
|
| |
|
|
| |
|
|
| |
|
|
| |
[ Applications (적용분야) ]
1. Manufacturing Photovoltaics (태양전지 제조)
2. Manufacturing Semi-Conductors (반도체 제조)
3. Missiles, Military industries, Heavy industries, Aerospace industries (미사일, 국방군수산업, 중공업, 항공우주산업)
4. Laboratories (연구실)
5. Precious metals, Steels, Metal Alloys, Nonferrous metals, Scraps, Residue, Minerals, Ores and, Coal (귀금속, 철, 합금, 비철, 고철, 광물질, 석탄 등.)
6. Precision casting (정밀주조)
7. Glass industries (유리산업)
8. Pharmaceuticals, Medicine, Chemicals, Fuel, etc. (제약 의료, 화학, 연료, 등.)
|
|
| |
|
|
| |
|
|
| |
|
|
| |
[ Physical and Chemical Properties (물리적 & 화학적 특성) ]
1. Chemical Composition (화학 조성)
| SiO2 |
99.9% |
| Al2O3 |
< 0.01% |
| Fe2O3 |
< 0.001% |
| Na2O + K2O |
< 0.005% |
2. Physical Properties (물리적 특성)
| Maximum Service Temperature (최고사용온도) |
℃ |
1650℃ |
| Bulk Density (부피비중) |
g/cm3 |
1.90 |
| Apparent Porosity (겉보기 기공율) |
% |
15 |
| Compressive Strength (압축강도) |
Mpa |
51.0 |
| Rupture modulus (곡강도) |
Mpa |
31.0 |
| Coefficient of Thermal Expansion (열팽창계수) |
10-6/ ℃ |
0.55 |
| Thermal Conductivity (열전도율) |
W/mK 1000℃ |
1.10 |
| Crystallinity (결정율) |
Vol % |
Under 1 |
|
|
| |
|
|
| |
|
|
| |
|
|
| |
[ Property of Fused Silica Crucible (용융석영도가니의 특성) ]
1.
Thermal Expansion Curves of Refractory Materials
(열팽창 곡선)
2.
Comparison of Thermal Conductivity with other Refractory Materials
(열전도도 곡선)
|
|
| |
|
|
| |
|
|
| |
|
|
| |
|
|
|